1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Kokvilnas audekla augstas temperatūras izturīgas jostas saķere ir salīdzinoši zema, un EP augstas temperatūras izturīgas jostas saķere ir salīdzinoši augsta; EP augstas temperatūras izturīgas jostas kalpošanas laiks acīmredzami ir ilgāks nekā kokvilnas audekla augstas temperatūras izturīgas jostas kalpošanas laiks.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Šī ir vēl viena līmēšanas metode, šī metode ir arī iespējama, taču, ja izmantojat šo metodi, pievērsiet uzmanību šādiem punktiem:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Parasti, ja vulkanizācijas temperatūra ir augstāka par paātrinātāja un vulkanizējošā līdzekļa kritisko vulkanizācijas temperatūru un nevar sasniegt parasto vulkanizācijas temperatūru, var izmantot vulkanizācijas laika pagarināšanas metodi, lai gumijas vulkanizācija atbilstu prasībām. Parasti katru reizi, kad temperatūra ir zemāka par 10 grādiem, vulkanizācijas laiks tiek pagarināts 2-4 reizes. Protams, veiktspējas apsvērumu dēļ mēs neiesakām izmantot zemu-temperatūru un ilgstošu vulkanizāciju.
5. Can core rubbers from different manufacturers be mixed?
Nav ieteicams jaukt dažādu ražotāju serdes gumiju, jo dažādu ražotāju serdes gumijas formula ir atšķirīga. Gumijā ir daudz dažādu savienojumu veidojošo vielu, un dažiem no tiem ir interaktīvas reakcijas. Viena un tā paša ražotāja formulā nebūs savienojumu ar negatīvām interaktīvām reakcijām, taču dažādu ražotāju formulas ir ļoti atšķirīgas. Lietojot, var būt interaktīvi savienojošo vielu atspulgi, kas ietekmēs gumijas serdes lietošanas efektu.